Aidmer-NA250

Data Sheet - 100% Non Asbestos

Compressed Non Asbestos Sheet Aidmer-NA250

ITEM	NA-250
Material	Made from Aramid Fiber, mineral fiber & inorganic fillers bonded with Synthetic NBR.
Application	Suitable for oil resistant gasket material for lower and medium loading, good resistance to water gases, oils and fuels
Properties	Test Method	Unit	Data range
Density	－	g/cm3	1.65 ~ 1.75
Max short term temperature		℃	400
Max continuous operating temperature with non aggressive media		℃	200
Max operating pressure		Mpa	8
Tensile Strength (across)	ASTM F152	N/mm2	≥10
Creep Relaxation	ASTM F38 16h @175°C	N/mm2	≤30
Compressibility	ASTM F36J	%	12±5
Recovery	ASTM F36J	%	≥45
ASTM3# oil 150℃／5h	Thickness increase	%	≤8
ASTM3# oil 150℃／5h	Weight increase	%	≤8
ASTM Fuel B 23℃／5h	Thickness increase	%	≤8
ASTM Fuel B 23℃／5h	Weight increase	%	≤8
Water/Antifreeze 1:1 100℃/5h	Thickness increase	%	≤5
Water/Antifreeze 1:1 100℃/5h	Weight increase	%	≤8
Dimension		mm	1500×1500
Thickness		mm	0.5、1.0、1.5、2.0、3.0

技术参数

产品型号：FRQ-250

产品名称：蓝色无石棉板

产品规格：1500×1500mm 1560×1500mm 4500×1500mm

产品厚度：0.2~5.0mm

材料描述：采用环保型芳纶浆粕纤维、人工合成纤维、耐油橡胶、环保填料，经过高温、高压辊压而成

应用领域：通用型的无石棉板材，适合于大多数对温度及压力要求不高的环境下使用，主要用于油、水及一般化学介质的密封

参考厚度： 1.5mm

技术参数	测试标准			单位		标准数值
密度	－			g/cm3		1.75~1.90
横向拉伸强度	ASTM F152			n/mm2		≥8
压缩率	ASTM F36J			%		10~17
回弹率	ASTM F36J			%		≥45
蠕变松弛率	ASTM F38 22h 100°C			%		≤40
泄露率	DIN 3535			ml/min		1.0
ASTM3# 油 150℃／5小时	厚度增加量			%		≤12
重量增加量		%	≤15
ASTM 燃油B 23℃／5小时	厚度增加量			%		≤10
重量增加量		%	≤10
工作温度	短时／连续			℃		250 / -50 ~ 200
工作压力	最大值			Bar		≤80

材质报告单

以NBR为粘合体，芳纶浆粕纤维为骨架材料，白炭黑、轻钙、硫酸钡、云母粉为填料

成分比例

其他化工原料